Properties of V8 Grades
|
材质 Grade |
电阻率Specific Elec. Resistivity (Ohm*m㎡/m) |
密度 Bulk density (g/cm³) |
电流密度 Current (A/c㎡) |
金属含量 Metal content (%) |
备注 Remarks |
|
V8 |
2.0 |
3.0 |
13 |
50 |
浸渍Impregnation |
1. The only copper-graphite billet in Europe that adopts two hot pressing synthesis process.
2. After hot pressing, the carbon blank has a uniform internal structure and is not easy to eccentrically wear in actual use.
3. Compared with the cold-pressed graphite blank, it can carry a larger working current and is suitable for low load and overload conditions.
4. It has good stability in extreme cold, high temperature, plateau, offshore and inland wind field environments.